|Hardness shore A||95±2||SHORE||ISO 868|
|Hardness shore D||48±3||SHORE||ISO 868|
|Tensile strength||≥50||MPa||DIN 53 504|
|Tear strength||≥110||kN/m||DIN ISO 34-1|
|Spec. gravity||1200||kg/m³||ISO 1183|
|Abrasion||17||mm³||DIN 53 516|
|modulus 100%||≥15||MPa||DIN 53 504|
|modulus 300%||≥28||MPa||DIN 53 504|
|Elongation at break||≥350||%||DIN 53 504|
|compression set 1||≥27||%||ISO 815|
|compression set 2||≥33||%||ISO 815|
|Min. service temperature||-20||C°|
|Max. service temperature||115||C°|
1 testing parameters 24h 70°C 25% Deflection
2 testing parameters 24h 100°C 25% Deflection
H-PU 95 Shore A is a universally applicable sealing material which can be characterized by its wide service temperature range.
This hydrolysis resistant PU can be used where other PU’s get broken already much earlier. The machinability by turning, milling and grinding is excellent.
H-PU has very good values for tensile strength, elongation at break and tear strength. It also has a very low compression set.
Its excellent wear resistance, high elasticity, high dynamic resistance as well as low permeability are other advantages. Additionally it is FDA certified. This material is injection molded and also casted available.